Density（g/cm³）

4.89

Melting Point(℃)

1280

Thermal Conductivity

11.72 Wm-1K-1 at 286K

Thermal Expansion

18.1 x 10-6 /℃ at 273K

Knoop Hardness

82 with 500g indenter (kg/mm2)

Specific Heat Capacity

410J/(kg.k)

Dielectric Constant

7.33 at 1MHz

Youngs Modulus (E)

53.07 GPa

Shear Modulus (G)

25.4 GPa

Bulk Modulus (K)

56.4 GPa

Elastic Coefficient

Elastic CoefficientElastic Coefficient

Apparent Elastic Limit

26.9 MPa (3900 psi)

Poisson Ratio

0.343