Density（g/cm³）

2.64

Melting Point（℃）

845

Thermal Conductivity

11.3 Wm-1K-1 at 314K

Thermal Expansion

37 x 10-6 /℃

Hardness (Mho)

113 with 600g indenter (kg/mm2)

Specific Heat Capacity

1562 J/(kg.k)

Dielectric Constant

9.0 at 100 Hz

Youngs Modulus (E)

64.79 GPa

Shear Modulus (G)

55.14 GPa

Bulk Modulus (K)

62.03 GPa

Rupture Modulus

10.8 MPa

Elastic Coefficient

C11=112; C12=45.6; C44=63.2